Methyl Phenyl Silicone Resin
Chemical Name: | Methyl Phenyl Silicone Resin |
Product Category: | Silicone Resin – Product |
Appearance: | Colorless transparent to light yellow liquid. |
Solid content %: | 50±1 |
Viscosity s/T-4,25℃: | 25-75 |
Drying time: | ≤2h/200℃ |
Heat tolerance: | >200h/200℃ |
Loss on heat 3h/250℃,%: | ≤3 |
Methyl Phenyl Silicone Resin Describe
Methyl phenyl silicone resin is mainly in liquid form, the color is colorless transparent to light yellow, milky white with light, without any mechanical impurities of the liquid, has excellent electrical insulation properties, high and low temperature resistance, water and moisture resistance, weather resistance, ozone resistance and chemical stability, and has good flexibility.
Methyl phenyl silicone resin can be dried quickly by finger pressure at room temperature and has a certain degree of hardness. After curing the coating can be used at 250-400°C. Some can withstand 500-600°C or even higher.
R1152
R1153
R1156C
RB01
RJ01
RJ02
Features:
It has excellent electrical insulation performance, high and low temperature resistance, water and moisture resistance, weather resistance, ozone resistance and chemical stability, and good flexibility.
Appearance | milk-white light alowed, no mechanical impurities, light yellow to reddish brown transparent liquid. |
Solid content % | ≥55 |
Viscosity s/T-4,25℃ | 25-75 |
Drying time | ≤2h/200℃ |
Heat tolerance | >200h/200℃ |
Loss on heat 3h/250℃,% | ≤3 |
Features and Main application | glass cloth used for the electric insulation of engines. |
It is widely used as the base resin for high temperature resistant coatings and special coatings, as well as general high and low temperature resistant insulating impregnating paints, covering paints (varnishes, paints, enamels, etc.), and H-class electrical insulating materials.
Usage :
1. According to the construction process, can be specified by adding diluent conditioning solid content and Viscosity. to control the thickness of the coating, usually adjusted for spraying viscosity 15-25 seconds; diluent should not contain water, sulfur and other impurities. The coating adhesive force will be affected, so was stem and other properties.
2. When in use, it should be avoided with acid and alkali, organic acids and amines contact, otherwise it will accelerate ageing, affect the performance of the product.
3. At work, according to the resin NO and the use of different requirements and then confirm dying condition, for high temperature dying type, it should be solvent dying to volatile at a lower temperature (120 or 160 ° C). Finally curing at 220 ℃.
4. Resin has good compatibility with heat resistant pigments (aluminum, glass bead, low-density ceramic powder. Black chromium oxide and iron oxide powder, etc.), the coating should be dipping, spraying, brush and other construction methods, curing the coating can be used in 250-400 ℃. Some may be resistant 500-600 ° C, even higher temperatures.
5. Application examples of reference:
(1) fire-resistant insulation coating formula :
silicone resin | Higher chlorinated polyethylene | epoxy resinF-644 | Polyamide resin | Padding | Flux | Titanate |
40-60Copies | 5-15Copies | 10-20Copies | 4-12Copies | 45-85Copies | 5-15Copies | 1-2Copies |
(2) fire-resistant aluminum section formula :
60% Methylphenyl silicone resin | 65%Aluminum Paste | xylene | Dispersant |
76Copies | 26Copies | 46Copies | 2Copies |
Safety Note :
1. Resin contains flammable, explosive and toxic solvents, In the process of use and processing, should pay attention to the site operation ventilation, to prevent fire, strengthening the protection of workers.
2. During transportation and storage, prevent sunlight, fire and heat protection, pay attention to warehouse ventilation.
3. Packed with galvanized iron sheet barrel, storage period is generally 6 months, if pass storage period, please test it strictly and then use. Avoid heat, otherwise it will reduce the storage stability.
Methyl Phenyl Silicone Resin R1153
Appearance | Colorless to light yellow transparent liquid, allowing milky white light without mechanical impurities |
Viscosity | 20-50 cst (closed 4 cup) |
Solid content, | 50±1 % |
Curing conditions, | ≤1h Copper sheet (200℃) |
Heat resistance | ≥300h (varnish sheet) Copper sheet (200℃) |
Thermal weight loss | ≤5 (250℃×3 hours)% |
Solvent | xylene |
Product description:
This product has excellent high and low temperature resistance, water and moisture resistance and good electrical insulation properties. It also has excellent weather resistant and chemical stability.
This product can be quickly surface-drying at room temperature. After complete curing, it has high hardness (≥2H), high gloss, good fullness, and no yellowing at high temperature. High temperature resistance grade.
IOTA 6156C is widely used as base resin for high temperature resistant coatings (400~600℃) and special coatings and H-class insulating coatings.
Technical index:
Appearance | light yellow to colorless transparent liquid, allowing milky white light, no mechanical impurities |
Solid content | 51±1% |
Viscosity | 15~45 seconds (coating 4 cups) |
Acid value | ≤4mgKOH/g |
Hardness after the varnish film is fully cured | ≥2H (Chinese pencil hardness) |
This product can be quickly dried by finger pressure at room temperature, and has a certain hardness. This product is completely cured by high temperature baking, 30 minutes at 250 °C; 20 minutes at 270 °C; 15 minutes at 280 °C
Methylphenyl Silicone Resin RB-1
Appearance | light yellow transparent viscous liquid |
Solid content % | 50±2 |
Viscosity s/T-4,25℃ | >50 |
Surface drying timeroom temperature | ≤3min |
Solvent | butyl acetate , butyl alcohol |
Features | rapidly form film in room temperature, high adhesive force, Moisture-proof antifouling, Pollution-resistant by black ink. (GB9274-88)≥9 |
Main application | antifouling of floor tiles and ceramic tile surface. |
Usage :
1. According to the construction process, can be specified by adding diluent conditioning solid content and Viscosity. to control the thickness of the coating, usually adjusted for spraying viscosity 15-25 seconds; diluent should not contain water, sulfur and other impurities. The coating adhesive force will be affected, so was stem and other properties.
2. When in use, it should be avoided with acid and alkali, organic acids and amines contact, otherwise it will accelerate ageing, affect the performance of the product.
3. At work, according to the resin NO and the use of different requirements and then confirm dying condition, for high temperature dying type, it should be solvent dying to volatile at a lower temperature (120 or 160 ° C). Finally curing at 220 ℃.
4. Resin has good compatibility with heat resistant pigments (aluminum, glass bead, low-density ceramic powder. Black chromium oxide and iron oxide powder, etc.), the coating should be dipping, spraying, brush and other construction methods, curing the coating can be used in 250-400 ℃. Some may be resistant 500-600 ° C, even higher temperatures.
5. Application examples of reference:
(1) fire-resistant insulation coating formula :
silicone resin | Higher chlorinated polyethylene | epoxy resinF-644 | Polyamide resin | Padding | Flux | Titanate |
40-60Copies | 5-15Copies | 10-20Copies | 4-12Copies | 45-85Copies | 5-15Copies | 1-2Copies |
All material will be transferred into a paste, and then grinding with sand mill 20 ~ 30min after the addition of solvent dispersion, and then filter.
(2) fire-resistant aluminum section formula :
60% Methylphenyl silicone resin | 65%Aluminum Paste | xylene | Dispersant |
76Copies | 26Copies | 46Copies | 2Copies |
Put aluminum paste into a container, add a small amount of resin, stir slowly, add disperser and residual resin, added xylene to construction of viscosity after fully stirred, with 120 mesh silk filter then finish.
Safety Note :1. Resin contains flammable, explosive and toxic solvents, In the process of use and processing, should pay attention to the site operation ventilation, to prevent fire, strengthening the protection of workers.
2. During transportation and storage, prevent sunlight, fire and heat protection, pay attention to warehouse ventilation.
3. Packed with galvanized iron sheet barrel, storage period is generally 6 months, if pass storage period, please test it strictly and then use. Avoid heat, otherwise it will reduce the storage stability.
Appearance | milk-white light alowed, no mechanical impurities, light yellow to reddish brown transparent liquid. |
Solid content % | ≥50 |
Viscosity s/T-4,25℃ | 20-55 |
Drying time | <3h/25℃ |
Heat tolerance | 300h/200℃ 0.5h/300℃ |
Features and Main application | 2K, room temperature curing, room temperature dying, suitable for large equipments used in high temperature. |
Usage :
1. According to the construction process, can be specified by adding diluent conditioning solid content and Viscosity. to control the thickness of the coating, usually adjusted for spraying viscosity 15-25 seconds; diluent should not contain water, sulfur and other impurities. The coating adhesive force will be affected, so was stem and other properties.
2. When in use, it should be avoided with acid and alkali, organic acids and amines contact, otherwise it will accelerate ageing, affect the performance of the product.
3. At work, according to the resin NO and the use of different requirements and then confirm dying condition, for high temperature dying type, it should be solvent dying to volatile at a lower temperature (120 or 160 ° C). Finally curing at 220 ℃.
4. Resin has good compatibility with heat resistant pigments (aluminum, glass bead, low-density ceramic powder. Black chromium oxide and iron oxide powder, etc.), the coating should be dipping, spraying, brush and other construction methods, curing the coating can be used in 250-400 ℃. Some may be resistant 500-600 ° C, even higher temperatures.
5. Application examples of reference:
(1) fire-resistant insulation coating formula :
silicone resin | Higher chlorinated polyethylene | epoxy resinF-644 | Polyamide resin | Padding | Flux | Titanate |
40-60Copies | 5-15Copies | 10-20Copies | 4-12Copies | 45-85Copies | 5-15Copies | 1-2Copies |
All material will be transferred into a paste, and then grinding with sand mill 20 ~ 30min after the addition of solvent dispersion, and then filter. (2) fire-resistant aluminum section formula :
60% Methylphenyl silicone resin | 65%Aluminum Paste | xylene | Dispersant |
76Copies | 26Copies | 46Copies | 2Copies |
Put aluminum paste into a container, add a small amount of resin, stir slowly, add disperser and residual resin, added xylene to construction of viscosity after fully stirred, with 120 mesh silk filter then finish.
Safety Note :1. Resin contains flammable, explosive and toxic solvents, In the process of use and processing, should pay attention to the site operation ventilation, to prevent fire, strengthening the protection of workers.
2. During transportation and storage, prevent sunlight, fire and heat protection, pay attention to warehouse ventilation.
3. Packed with galvanized iron sheet barrel, storage period is generally 6 months, if pass storage period, please test it strictly and then use. Avoid heat, otherwise it will reduce the storage stability.
Appearance | milk-white light alowed, no mechanical impurities, light yellow to reddish brown transparent liquid. |
Solid content % | ≥50 |
Viscosity s/T-4,25℃ | ≥20 |
Drying time | <1h/25℃ |
Curing time | 2h/180℃ |
Heat tolerance | 2h/300℃ |
Features and Main application | room temperature fast drying, high hardness, high adhesive force, good heat resistance. |
Usage :
1. According to the construction process, can be specified by adding diluent conditioning solid content and Viscosity. to control the thickness of the coating, usually adjusted for spraying viscosity 15-25 seconds; diluent should not contain water, sulfur and other impurities. The coating adhesive force will be affected, so was stem and other properties.
2. When in use, it should be avoided with acid and alkali, organic acids and amines contact, otherwise it will accelerate ageing, affect the performance of the product.
3. At work, according to the resin NO and the use of different requirements and then confirm dying condition, for high temperature dying type, it should be solvent dying to volatile at a lower temperature (120 or 160 ° C). Finally curing at 220 ℃.
4. Resin has good compatibility with heat resistant pigments (aluminum, glass bead, low-density ceramic powder. Black chromium oxide and iron oxide powder, etc.), the coating should be dipping, spraying, brush and other construction methods, curing the coating can be used in 250-400 ℃. Some may be resistant 500-600 ° C, even higher temperatures.
5. Application examples of reference:
(1) fire-resistant insulation coating formula :
silicone resin | Higher chlorinated polyethylene | epoxy resinF-644 | Polyamide resin | Padding | Flux | Titanate |
40-60Copies | 5-15Copies | 10-20Copies | 4-12Copies | 45-85Copies | 5-15Copies | 1-2Copies |
All material will be transferred into a paste, and then grinding with sand mill 20 ~ 30min after the addition of solvent dispersion, and then filter. (2) fire-resistant aluminum section formula :
60% Methylphenyl silicone resin | 65%Aluminum Paste | xylene | Dispersant |
76Copies | 26Copies | 46Copies | 2Copies |
Safety Note :
1. Resin contains flammable, explosive and toxic solvents, In the process of use and processing, should pay attention to the site operation ventilation, to prevent fire, strengthening the protection of workers.
2. During transportation and storage, prevent sunlight, fire and heat protection, pay attention to warehouse ventilation.
3. Packed with galvanized iron sheet barrel, storage period is generally 6 months, if pass storage period, please test it strictly and then use. Avoid heat, otherwise it will reduce the storage stability.
Packaging Specifications


Jessica G.
Get in touch to Get
- Quick and helpful reply within 8 hours;
- Tailored solutions provided for your project;
- One-stop purchasing service.
Methyl Phenyl Silicone Resin : Guide
One of the Phenyl methyl hydrogen silicone resin with hydrogen cyclic D4H, imported D4, phenyl monomers as raw materials, synthesized by a special post-processing process of hydroxymethyl phenyl silicone resin, with good Si-H activity, is the manufacture of high-temperature liquid molded silicone rubber crosslinking agent, a reliable high refractive index phenyl LED encapsulation silica gel.